| Carbon Steel & Stainless Steel Cut Wire Shot |
| Carbon Steel & Stainless Steel Cut Wire shot are widely used for shot peening to give compressive residual stress in the surface layer of components for fatigue life enhancement and suppression of stress corrosion cracking as well as cleaning and polishing of the surface of metal parts, deburring of die cast parts, is of reusable and recyclable, the working life is 1000 times of glass bead, can produce very bright surface, but creat much less dust than glass beads, natural and artificial corundum abrasives. The hardness is 20-40HRC. |
|
| |
|
|
| Stainless steel cut wire shot |
Conditioned stainles steel cut wire shot |
|
| |
| Chemical Composition (% by weight) |
|
C |
Cr |
Ni |
Si |
Mn |
S |
P |
| |
|
|
|
max |
|
max |
max |
Stainless steel cut wire shot (SUS202) |
0.15 max |
17.0-19.0 |
4.0-6.0 |
1.0 |
7.5-10.0 |
0.03 |
0.06 |
stainless steel cut wire shot (SUS304) |
0.07max |
17.0-19.0 |
8.0-10.0 |
1.0 |
2.0 max |
0.035 |
| Stainless steel cut wire shot (SUS316) |
0.08 max |
16.0-18.5 |
10.0-14.0 |
1.0 |
2.0 max |
0.035 |
Stainless steel cut wire shot (SUS430) |
0.12 max |
16.0-18.0 |
0 |
0.75 |
1.25 max |
0.035 |
| Carbon steel cut wire shot |
0.45-0.75 |
- |
- |
0.1-0.3 |
0.3-1.2 |
0.05 |
0.05 |
|
| |
| Available Sizes |
| Material |
stainless steel cut wire shot |
Conditioned stainless steel cut wire shot (SUS304) |
carbon steel cut wire shot |
| (SUS430) |
(SUS304) |
Size(mm) |
300-450 HV |
400-500 HV |
500 HV |
HRC45-50 |
| 0.3 |
v |
v |
v |
- |
| 0.4 |
v |
v |
v |
- |
| 0.5 |
v |
v |
v |
- |
| 0.6 |
v |
v |
v |
- |
| 0.7 |
v |
v |
v |
- |
| 0.8 |
v |
v |
v |
v |
| 1.0 |
v |
v |
v |
v |
| 1.2 |
v |
v |
v |
v |
| 1.5 |
v |
v |
v |
v |
| 2.0 |
v |
v |
v |
v |
| 2.5 |
v |
v |
v |
v |
|
| |
 |
| Aluminium, Zinc & Copper Cut Wire Shot |
| |
Zinc cut wire, Aluminium cut wire shot and Copper cut wire shot are made of zinc wire, aluminium wire and copper wire respectively, widely used for shot peening to give compressive residual stress in the surface layer of components for fatigue life enhancement and suppression of stress corrosion cracking and deburring and cleaning of zinc or aluminum die cast parts, without any damage to the parts, and creating much less dust than natural and artificial corundum abrasives. Zinc & Aluminium cut wire are of reusable and recyclable, have longer work life than natural and artificial corundum abrasives. |
| |
|
| |
| Chemical Content |
|
Zn |
Zinc Cut Wire shot ZN-1 (HV
35-55) |
99.99 |
|
Al |
Aluminium Cut Wire shot AW5056 (HV 95-125) |
99.7 |
|
Cu |
Copper Cut Wire shot |
96-99 |
| Brass cut wire shot |
62 |
|
|
| |
| Available Sizes ,in mm |
Zinc Cut Wire shot ZN-1 (HV 35-55) |
0.6mm |
0.7mm |
0.8mm |
1.0mm |
1.2mm |
1.5 mm |
1.8mm |
2.0mm |
2.5mm |
Conditioned Zinc Cut Wire shot ZN-1 (HV 45-60)
|
|
|
v |
v |
v |
v |
v |
v |
v |
Aluminium Cut Wire shot |
v |
v |
v |
v |
|
v |
|
v |
v |
Copper Cut Wire shot |
v |
|
v |
v |
|
v |
|
v |
v |
Brass Cut Wire shot |
v |
|
v |
v |
|
v |
|
v |
v |
|
| |